A thin film of titania (TiO2) was deposited onto AISI 316L steel using physical vapour deposition (PVD). Coating thickness was measured using Elecometer instrument and it was (150µm).Corrosion resistance to (H2SO4,HCl, H3PO4, and HF) acids with (2&4) pH, and to (NaOH, KOH,Ca(OH)2, and NH4OH) basis with (10,12) pH, of coated specimen was measured at temperatures ranges from (25-190) Co by weight loss method. It has been found that TiO2 coating largely enhance corrosion resistance of steel alloy especially at high temperatures.
Saadoon Mohsin,A . (2016). THE EFFECT OF PH AND TEMPERATURE ON CORROSION RESISTANCE OF TIO2 COATED AISI 316L STEEL. Al-Qadisiyah Journal for Engineering Sciences, 9(3), 360-367.
MLA
Saadoon Mohsin,A . "THE EFFECT OF PH AND TEMPERATURE ON CORROSION RESISTANCE OF TIO2 COATED AISI 316L STEEL", Al-Qadisiyah Journal for Engineering Sciences, 9, 3, 2016, 360-367.
HARVARD
Saadoon Mohsin A. (2016). 'THE EFFECT OF PH AND TEMPERATURE ON CORROSION RESISTANCE OF TIO2 COATED AISI 316L STEEL', Al-Qadisiyah Journal for Engineering Sciences, 9(3), pp. 360-367.
CHICAGO
A Saadoon Mohsin, "THE EFFECT OF PH AND TEMPERATURE ON CORROSION RESISTANCE OF TIO2 COATED AISI 316L STEEL," Al-Qadisiyah Journal for Engineering Sciences, 9 3 (2016): 360-367,
VANCOUVER
Saadoon Mohsin A. THE EFFECT OF PH AND TEMPERATURE ON CORROSION RESISTANCE OF TIO2 COATED AISI 316L STEEL. QJES. 2016;9(3):360-367.